Transparent PC Uncoated / Coated Overlay Film Suitable for Laser Engraving Card Making Process
Transparent PC Uncoated / Coated Overlay Film is specially designed for laser engraving feature on card surface. After lamination, it can leave clear and neat laser marks on card surface. Comparing with other types of plastic films for card body production, it excels in outstanding optical clarity, printability, impact strength and dimensional stability.
1.Transparent PC Uncoated / Coated Overlay Film - Introduction
Brief Introduction:
PC Uncoated/Coated Overlay Film could be lasering and customization, excels in outstanding optical clarity, printability,
impact strength, and dimensional stability when compared with other types of plastic films.
● Work well at high temperature,no color change with fluorescent ink.
● Abrasion resistant , prolong the life of cards.
● Environment friendly, no solvent or gas discharged.
| Item | Specification | Test Method | |
| Thickness | 40-100um | ||
| Thickness tolerance | ＞0.5±6um ≤0.5±4um | ||
| Density | 1.2±0.05 g/cm3 | ASTM D792 | |
| Surface tension(front) | ≥34Dynes/cm | ASTM D1922 | |
| Surface tension(back) | ≥34Dynes/cm | ASTM D1922 | |
Heating Shrinkage (%) (135℃±2,10min) | Thickness≤ 0.175mm | MD | ≦2.5 |
| CD | ≦0.5 | ||
| Vicat | 147±20C | ASTM D1525 | |
| Tensile strength | ≥50 N/mm2 | ISO527-3 | |
| Surface roughness | 0.5um-1.8um | ||
2.Transparent PC Uncoated / Coated Overlay Film- Parameters
1). Size: in sheet or reel, A4, A3 or as per customer requirements
2). Normal thickness in mm: 0.04,0.05,0.06,0.08,0.10
3). Color: transparent, with/without coating on surface are both ok.
4). Package method: in reel or 500 sheets per bag/4 bags per paper carton, or as per customer requirements.
5). Storage condition: Sealed, moisture-proof, room temperature under 40℃, Keep it horizontally, avoid heavy pressing and direct sunlight.
6). Laser engraving performance: can be laser engraved.
| Technical parameters | |||
| Item | Standard Value | ||
Thickness (mm) | 0.04-0.1 ( ±5%) | ||
| Surface | Matt/Matt, flat, no defect, no dust. | ||
| Tensile Strength (Mpa) -ISO527-3 | ≧50(MD/CD) | ||
| Break Strength (%) -ISO527-3 | ≧60(MD/CD) | ||
Folding Capacity | Thickness <0.25mm, ≧13 | ||
| Thickness ≧0.25mm,≧11 | |||
| Light Transmittance (%) | ≧80 | ||
| Haze (%) | ≦ 90 | ||
| Surface Tension(Dynes/cm) -ISO 8296-2003 | ≧34 | ||
Heating Shrinkage (%) (135℃±2,10min) | Thickness≤ 0.175mm | MD | ≦2.5 |
| CD | ≦0.5 | ||
| Vicat Softening Temperature(℃) - ISO 306-1994 | 150±3 | ||
| Coating availability | with coating or w/o coating are both OK. | ||
3.Transparent PC Uncoated / Coated Overlay Film - Application
such as identity card,driving card, passport etc.
| Item | Parameters | |
| Vicat (℃) | 147±2 | |
| Shrinkage | MD/TD | ＜1.0 |
| Tensile Strength (MPa) | MD | ≥50 |
| TD | ≥50 | |
| Roughness(μm) | Ra | 0.58, 1.5-2.1 |
| Ra | 3.45 | |
| Thickness(mm) | 0.04-0.1 | |
◆Laminating Condition:
| Laminating Unit | Temp(℃) | Pressure(MPa) | Time (min) |
| Heat Laminating | 140~155 | ≥6 | 25 |
| Cool Laminating | ≤25 | ≥6 | 15 |
Card-making method:
1. Print the patterns directly to the material
2. Laminate with overlay
3. Punching
4. Other art-work
4.Transparent PC Uncoated / Coated Overlay Film - Packing
Packing:
Outer:Carton Inner:PE bag
Storage:
Keep package sealed and moisture-proof, room temperature under 40℃
Keep horizontally, avoid oppress heavily and direct sun light.
Stacking height should not exceed one meter.
Shelf life: Two years.
Storage conditions:
Ideal storage conditions under 40℃ of room temperature, Ideal RH 40%. Should not be stored in direct sunlight and avoid major thermal fluctuation, store in original packing. Film should be conditioned a minimum of 24 hours at ambient room temperature.
Recommended use of material within one year of production date.
|
|