Laserable Polycarbonate Overlay Transparent 0.10mm 0.80mm PC
Plastic Sheet
1. Product Introduction of Laserable Polycarbonate Overlay
Transparent 0.10mm 0.80mm PC Plastic Sheet
Polycarbonate overlay is specially designed for laser engraving
feature on card surface. After lamination, it can leave clear and
neat laser marks on card surface. Comparing with other types of
plastic films for card body production, it excels in outstanding
optical clarity, printability, impact strength and dimensional
stability.
| Item | Unit | Value | |
| Density | g/cm3 | 1.30 ±0.05 | |
| Tensile Strength | Horizontal | MPa | ≥50 |
| Vertical | ≥50 | ||
| Vicat | ℃ | 145±2 | |
| Surface Dyne | dynes/cm | ≥38 | |
2. Product Features of Laserable Polycarbonate Overlay Transparent
0.10mm 0.80mm PC Plastic Sheet
Parameters:
1. Size: in sheet or reel, A4, A3 or as per customer requirements
2. Normal thickness in mm: 0.04,0.05,0.06,0.08,0.10
3. Color: transparent without coating on surface.
4. Package method: in reel or 500 sheets per bag/4 bags per paper
carton, or as per customer requirements.
5. Storage condition: Sealed, moisture-proof, room temperature
under 40℃, Keep it horizontally, avoid heavy pressing and direct
sunlight.
6. Perfect image of laser etching technology support, apply to
identity cards with anti-fake requirements.
| Technical parameters | |||
| Item | Standard Value | ||
Thickness (mm) | 0.04-0.085 ( ±5%) | ||
| Surface | Matt/Matt, flat, no defect, no dust. | ||
| Tensile Strength (Mpa) -ISO527-3 | ≧50(MD/CD) | ||
| Break Strength (%) -ISO527-3 | ≧60(MD/CD) | ||
Folding Capacity | Thickness <0.25mm, ≧13 | ||
| Thickness ≧0.25mm,≧11 | |||
| Light Transmittance (%) | ≧80 | ||
| Haze (%) | ≦ 90 | ||
| Surface Tension(Dynes/cm) -ISO 8296-2003 | ≧34 | ||
Heating Shrinkage (%) (135℃±2,10min) | Thickness≤ 0.175mm | MD | ≦2.5 |
| CD | ≦0.5 | ||
| Vicat Softening Temperature(℃) - ISO 306-1994 | 150±3 | ||
| Coating availability | No coatings on both sides | ||
3. Testing report of Laserable Polycarbonate Overlay Transparent
0.10mm 0.80mm PC Plastic Sheet
| Feature | Testing method | Unit | Testing value |
| Physics | |||
| Specific gravity | ASTM D792 | G/cm³ | 1.2 |
| Average water absorption | ASTM D570 | % | 0.35 |
| Mechanical | |||
| Tensile strength | ASTM D882 | Psi | 8800 |
| ISO R1184-1987 | Mpa | 60 | |
| Ultimate elongation | ASTM D882 | % | >90 |
| Impact strength | JIS-k6745 | In-ibs | 120 |
| Tear strength | ASTM D1922 | G/mil | >30 |
| Temperature resistance | |||
| Vicat softening point | ASTM D1525 | ℃ | 128 |
| Thermal shrinkage | D1204 | % | <1.0 |
| Electrical | |||
| Dielectric strength | ASTM D149 | V/mil | 1700 |
| Volume Insulation | ASTM D257 | Ohm.m |  |
| Surface Insulation | ASTM D257 | Ohm |  |
| Roughness value | |||
| Medium sand | um | Ra3.45 | |
| Fine sand | um | Ral.5~2.1 | |
| Matte | um | Ra0.58 | |
| Feature | unit | limit | |
| Thickness tolerance | % | >0.5±0.006mm | |
| ≤0.5 ±0.004mm | |||
|
|